Bauderflex Reinforced Bitumen Membrane Cold Roof Covering System Self-Adhered (with Torch-On Capping Sheet)

Activator-Primer (Canister) APR01 - Black.

Guidance for specification option:

Synthetic rubber resin-based primer, developed to provide the necessary preparation of substrates prior to the installation of self-adhesive and torch-applied membranes. The spray application offers improved film thickness speed of application (by up to 50% over roller applied products) and quick drying in a matter of minutes.

• Coverage: approximately 96 g/m² (300 mm-wide spray one coat, 192 g/m² two coats). Two coats may be required for very porous substrates.
• Application temperature: +5 to +30°C.
• Drying time (at 10°C): 5–10 minutes.
• Colour: black.
• Recoat time if left exposed: four hours.
• Suitable substrates: oriented strand board (OSB); plywood; timber; concrete; lightweight concrete or cementitious materials; metal; Bauder self-adhesive underlayers; existing asphalt and bitumen membranes; polyisocyanurate (PIR) insulation.
• Non-suitable substrates: mica-finished surfaces (e.g. KSD FBS); Laminated paper-foil faced insulation; expanded polystyrene (EPS) or extruded polystyrene (XPS) insulations; BauderROCK or mineral wool insulation; BauderGLAS or cellular glass insulation; copper; thermoplastic waterproofing membranes.

SA Bonding Primer.

Guidance for specification option:

For Self-Adhesive membranes to Concrete and Screeded Substrates.

Synthetic rubber-based primer, specially formulated to increase the bond strength of Bauder self-adhesive bitumen membranes to a wide range of substrates, including timber, concrete, brick, metal and most plastics.

• Coverage: approximately 200–300 g/m² (depending on substrate porosity).
• Application temperature: +5 to +30°C.
• Drying time: approximately 30 minutes, dependent upon ambient temperature and material porosity.
• Colour: black.
• Recoat time if left exposed: four hours.
• Suitable substrates: timber, concrete, brick, metal and most plastics.

BauderTEC Sprint DUO.

Guidance for specification option:

Elastomer bitumen self-adhesive underlayer with variable technology for lap sealing. The two side laps of the membrane have differing finishes. On one lap there is a self-adhesive finish, whist the opposite lap has a glass fleece. This allows the membrane to be sealed with either a gas torch or hot air welder.

• Width: 1 m.
• Length: 15 m.
• Thickness: 2 mm.
• Weight: 2.5 kg/m².
• Surface, top: foil; bottom: peel-off release film covering self-adhesive bitumen.
• Reinforcement: 200 g/m² glass lattice.
• Cold bending test: -30°C.
• Softening point: >100°C.
• Tensile strength: length >1000 N/50mm; transverse >1000 N/50mm.
• Elongation at break: length >2%; transverse >2%.

Bauder PYE PV 200 S4.

Guidance for specification option:

Torch-applied, elastomeric bitumen, mica-finished capping sheet, 4.2 mm thick. Features a spun-bound polyester reinforcement to allow the finished product to cope with structural movement without fracture. Its mica finish means that it has no integrated UV protection, therefore is only suitable for applications where it will be covered with hard landscaping, such as pavers or promenade tiles.

• Width: 1 m.
• Length: 10 m.
• Thickness: 4.2 mm.
• Weight: 5 kg/m².
• Surface, top: mica; bottom: thermofusible polyethylene.
• Reinforcement: 250 g/m² recycled, spun-bound polyester.
• Cold bending test: -25°C.
• Softening point: >100°C.
• Tensile strength: length >800 N/50mm; transverse >800 N/50mm.
• Elongation at break: length >35%; transverse >35%.

BauderFLEX K4E, Brown.

Guidance for specification option:

Elastomer bitumen torch-on capping sheet. The product features a spunbond polyester reinforcement to allow the finished product to cope with structural movement without fracture, and a mineral finish to provide protection against UV degradation. Product has been fire tested as part of a system assembly and this information can be obtained in the Fire Test Report available from Bauder Ltd.

• Width: 1 m.
• Length: 7.5 m.
• Thickness: 4.2 mm.
• Weight: 5 kg/m².
• Surface, top: mineral chippings.
• Reinforcement: 250 g/m² spun-bound polyester.
• Cold bending test: -30°C.
• Softening point: >110°C.
• Tensile strength: length >800 N/50mm; transverse >800 N/50mm.
• Elongation at break: length >40%; transverse >40%.

BauderFLEX K4E, Charcoal Grey.

Guidance for specification option:

Elastomer bitumen torch-on capping sheet. The product features a spunbond polyester reinforcement to allow the finished product to cope with structural movement without fracture, and a mineral finish to provide protection against UV degradation. Product has been fire tested as part of a system assembly and this information can be obtained in the Fire Test Report available from Bauder Ltd.

• Width: 1 m.
• Length: 7.5 m.
• Thickness: 4.2 mm.
• Weight: 5.5 kg/m².
• Surface, top: mineral chippings.
• Reinforcement: 250 g/m² spun-bound polyester.
• Cold bending test: -30°C.
• Softening point: >110°C.
• Tensile strength: length >800 N/50mm; transverse >800 N/50mm.
• Elongation at break: length >40%; transverse >40%.

BauderFLEX K4E, Grey Slate.

Guidance for specification option:

Elastomer bitumen torch-on capping sheet. The product features a spunbond polyester reinforcement to allow the finished product to cope with structural movement without fracture, and a mineral finish to provide protection against UV degradation. Product has been fire tested as part of a system assembly and this information can be obtained in the Fire Test Report available from Bauder Ltd.

• Width: 1 m.
• Length: 7.5 m.
• Thickness: 4.2 mm.
• Weight: 5 kg/m².
• Surface, top: mineral chippings.
• Reinforcement: 250 g/m² spun-bound polyester.
• Cold bending test: -30°C.
• Softening point: >110°C.
• Tensile strength: length >800 N/50mm; transverse >800 N/50mm.
• Elongation at break: length >40%; transverse >40%.