Fire Protection FIRETEX® Platinum - Fire Protection Coating
Verified by manufacturer 5 months ago
FIRETEX® Platinum-120
FIRETEX® Platinum-120
A solvent and Halogen-free, 100% solids, two pack, modified epoxy based intumescent fire protection coating.
Application
Applied directly on to blast cleaned steel surfaces by airless spray.
Description
A solvent and halogen-free, 100% solids, two pack, modified epoxy based intumescent fire protection coating for internally or externally exposed structural steel, where it provides highest durability and combined corrosion protection (up to ISO 12944, corrosivity category C5) and fire protection (up to R120).
Features and benefits:
- Highly resistant to mechanical impact and damage.
- No primer required
- Complies with the sustainability requirements of DGNB (level 3).
- Long life cycle of >25 years.
- Up to 120 minutes of fire resistance.
- CE marked.
- Tested to EN 13381-8, BS 476 part 20-22 and EN 13501-2.
- Complies with Indoor Air Comfort Gold.
- Topcoats can be applied to provide final colour as desired.
General information
Color | Grey |
Finish | Gloss |
Material | Epoxy |
Shape | Formless |
Length | Bespoke |
Width | Bespoke |
Height | Bespoke |
Warranty description | 25 year |
Uniclass | |
CAWS | M61/150 Off-site coating to unprimed steel M61/160 Off-site coating to primed steel M61/170 Off-site coating to galvanized steel G10/640 Shop painting G10/660 Shop plus site painting |
Specification data - Intumescent protective coatings
Composition | Epoxy-borne. |
Colour | Light grey. |
Flash point | >101°C (base and hardener). |
Density | 1.3 kg/L. |
Application temperature | 10–40°C. |
Abrasion resistance | To ISO 5470-1, ~65 mg/ 1000 R. |
CompressiveStrength | To ISO 604, ~45 MPa. |
TensileStrength | To ISO 527-2, ~10 MPa. |
Adhesion strength | To EN ISO 4624, ~10 N/mm². |
Coverage | 0.77 m²/kg will cover 1.00 m²/L. Guidance for specification option: This figure makes no allowance for surface profile, uneven application, overspray or losses in containers and equipment. |
Drying time | Eight hours to touch (at 20°C); 24 hours to handle (at 20°C). |
Fire resistance | R120. |
Similar products from Sherwin-Williams
Fire Protection FIRETEX® FX2003
Fire Protection FIRETEX® FX5062
Fire Protection FIRETEX® FX5090
Fire Protection FIRETEX® FX6002
Fire Protection FIRETEX® FX6010
Fire Protection FIRETEX® M71V2