Verified by manufacturer 4 months ago
A two-component semi-gloss acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention.
Finishing coat for protection of structural steel in a corrosive environment.
To Specify a full Intumescent Fire Protection Coating System C1-C4 (Primer + Intumescent + Topcoat) click on the link below and add to your Chorus Specification:
To Specify a full Anti-Corrosion System C1-C5 (No Intumescent Fire Protection) (Primer + Topcoat) click on the link below and add to your Chorus Specification :
For further advice on Specifications please contact Ian Morton at iam@hempel.com
Hempathane HS 55613
A two-component semi-gloss acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention.
Features and benefits:
Product compatibility:
Application method:
Drying time:
Determined for dry film thickness 100 µm (3.9 mils) at standard conditions. Indicative value at 20ºC; Hard dry: Six hours.
Color | Grey Manufacturer guidance11150* / Grey |
Finish | Semi-gloss |
Material | Polyurethane |
Shape | Formless |
Length | Bespoke |
Width | Bespoke |
Height | Bespoke |
Uniclass | |
CAWS | G12/30 Proprietary G12/330 Proprietary metal members G10/650 Site painting G10/640 Shop painting G10/660 Shop plus site painting G10/643 Protective painting M60/18 Special coating M60/195 Special coating M60/175 Protective coating |
Composition | A two-component semi-gloss acrylic polyurethane topcoat, cured with aliphatic isocyanate, with good gloss and colour retention. |
Sheen | Semi-gloss. |
Colour | 11150/ Grey. |
Volume solids | 57 ±2%. |
Flash point | 31°C (87.8°F). |
Specific gravity | 1.4 kg/L (11.4 lbs/US gallon). |
Fully cured | Seven days 20°C (68°F). |
VOC content | 387 g/L (3.23 lbs/US gallon). |
Shelf life | Three years. Manufacturer guidance3 years for BASE and 2 years (25°C/77°F) for CURING AGENT from time of production. |
Standard | Complies with EU Directive 2004/42/EC: subcategory j. |