A polymer-modified binder for use in rapid-set cement screeds allowing early flooring installation.
For indoor and outdoor use.
A special polymer-modified binder for use in rapid-set cement screeds allowing early flooring installation, based on DIN 18 560. Low-chromate to Regulation 1907/2006/EC, Annex XVII.
Features and benefits:
Mixing ratio:
Particle distribution (grading curve) for aggregate (screed sand) shall fall within A8/B8 range under DIN 1045 Part 2, Annex L, Diagram L.1, and shall exhibit an adequate, though not overly high proportion of fine sand; percentage passing a 0.25 mm sieve: approx. 7–10 %.
Coverage:
Strength class:
- Mixing ratio 1:4:
- Mixing ratio 1:5:
Color | Grey |
Uniclass | |
CAWS | M10/110 Bonded cement:sand levelling screeds M10/115 Cement:sand levelling screeds M10/12 Proprietary polymer modified levelling screeds M10/130 Proprietary quick drying levelling screeds M10/140 Proprietary polymer modified levelling screeds M10/7 Proprietary quick drying levelling screeds M40/320 Existing concrete/ screeds |
Product range |
Colour | Cement grey. |
Thickness | Maximum and minimum screed thickness depends on incorporated aggregate. Screed should be at least three times and at most ten times as thick as maximum particle diameter of aggregate. Recommended grading of screed aggregate 0–8 mm; coat thickness approximately 25–80 mm. |
Pot life | 2–3 hours (approximately). Guidance for specification option: Stiffened mortar must not be retempered by addition of water or fresh mortar to restore workability. |
Drying time | Walkable: After 7–8 hours; Ready to receive floor covering: For tiling: after approx. three days; for impervious coverings: after 3–5 days and after achievement of residual moisture content ≤1.8% CM. |
Application temperature | 5–25°C. |
Minimum thickness | Floor heating systems, 25 mm pipe cover. |
Suitability for castor chairs | Suitable (for castors to DIN 68131). Manufacturer guidance(Castor chair resistance) |
Contains Red List materials | No |
Country of material origin | Germany |
Country of product manufacture | Germany |
Manufacturing plant location | |
Embodied carbonA1-A3 (production stage) as defined in BS EN 15804 | 4.88 kg CO₂ eq/kg |
NBS BIM Object Standard
This BIM object has been authored to meet the requirements of the NBS BIM Object Standard.
Find out more about the NBS BIM Object Standard.
Platform | Compatible | Version |
---|---|---|
- | 3 | |
Revit 2017 | 3 |