Sikaflex®-113 Rapid Cure - Construction adhesive

Name: Sikaflex®-113 Rapid Cure - Construction adhesive
Brand: Sika Limited
SKU: fxFNtZjuoNP351w5Edk95f

Verified by manufacturer over a year ago

Sika Limited

Fast curing construction adhesive.

Jump to:

+44 (0)1707 394444 Website

Application

For internal and external use. An adhesive to bond most construction components and materials such as:

Concrete.
Masonry.
Most stones.
Ceramic.
Wood.
Metals.
Glass.

Description

A one-part, fast curing adhesive with very high initial grab which bonds most common construction substrates.

Features and benefits:

Fast curing.
Early handling after 20 minutes.
Compatible with with EPS/ XPS.
Adhesive-sealant with CE marking.
Very low emissions.

Approvals/ standards:

CE Marking and Declaration of Performance to EN 15651-1 - Sealants for non-structural use in joints in buildings - Facade elements: Class F EXT-INT 12,5P.

Environmental information:

Conformity with LEED v4 EQc 2: Low-Emitting Materials.
VOC emission classification GEV-EMICODE EC 1PLUS.
VOC emission classification of building materials RTS M1.
Class A+ according to French Regulation on VOC emissions.

General information

Color	White Black
Material	Silane Polymer
Shape	Formless

Uniclass	Pr_30_31_76_16 Construction joint sealantsPrimary
CAWS	H51/610 Sealant joints E40/530 Sealant F30/610 Movement joints with sealant H13/750 Structural sealant joints H13/740 Sealant joints F30/76 Movement joints with sealant M40/75 Sealant movement joints H51/610 Sealant joints H40/785 Sealant jointing H42/661 Sealant joints E40/530 Sealant H42/661 Sealant joints

Specification data - Construction joint sealants

Standard	To EN 15651-1.
Material	Single-part polymer.
Class	F-12.5P.
Colour	White. Black.
Fire performance	-
Reaction to fire	Class E.

Base	Silane terminated polymer. Manufacturer guidance Chemical base.
Density	To ISO 1183-1, ~1.50 kg/l.
Shore A hardness	To ISO 868, ~55. Guidance for specification option: After 28 days.
TensileStrength	To ISO 37, ~2.5 N/mm².
Elongation at break	To ISO 37, ~350%.
ShearStrength	To ISO 17178, ~0.9 MPa (1 hour); ~1.9 MPa (24 hours); ~2.4 MPa (7 days). Guidance for specification option: At 23°C/ 50 % r.h, 0.1 mm thickness. Manufacturer guidance Lap shear strength.
Tear resistance	To ISO 34, ~6.0 N/mm.
Service temperature	−40 to +60°C.
SAG	To ISO 7390, ~1 mm. Guidance for specification option: 20 mm profile, 23°C. Manufacturer guidance Sag flow.
Ambient temperature	5–35°C. Guidance for specification option: Minimum–maximum.
Substrate	5–35°C. Guidance for specification option: Minimum–maximum, 3°C above dew point temperature. Manufacturer guidance Substrate temperature.
Curing time	~4 mm/ 24 h. Guidance for specification option: 23°C/ 50% r.h. Skin time (CQP 019-1): ~12 min, 23°C/ 50% r.h. Manufacturer guidance CQP 049-2.

Sikaflex®-113 Rapid Cure - Construction adhesive

Application

Description

General information

Color

Material

Shape

Uniclass

CAWS

Specification data - Construction joint sealants

Standard

To EN 15651-1.

Material

Single-part polymer.

Class

F-12.5P.

Colour

White.

Black.

Fire performance

Reaction to fire

Class E.

Base

Manufacturer guidance

Density

Shore A hardness

TensileStrength

Elongation at break

ShearStrength

Manufacturer guidance

Tear resistance

Service temperature

SAG

Manufacturer guidance

Ambient temperature

Substrate

Manufacturer guidance

Curing time

Manufacturer guidance