webertec EP pourable grout - Epoxy Resin Grout

Name: webertec EP pourable grout - Epoxy Resin Grout
Brand: Saint-Gobain Weber
SKU: tDGsvPuxeaf7UGWLLaXbvU

Verified by manufacturer 4 months ago

Third party certifications:

High-strength, chemically-resistant grout.

Jump to:

Application

Suitable for the following:

Bearings.
Starter bars.
Dowels.
Balustrading.
Crane rails.
Machine baseplates.
Setting-in bolts.
Fixing runway lights.
Situations where tight clearances add to the difficulties of obtaining secure fixings.
Filling gaps of between 5–75 mm.

Do not apply below 5°C.

Three-component pourable grout, formulated from epoxy resin and graded aggregates.

Features and benefits:

Complies with BS EN 1504-3 and -6.
Capable of withstanding high dynamic loads.
High compressive and tensile strength.
Very good chemical resistance.
Cures within the temperature range 5–35°C.
Negligible shrinkage factor allows use for underplate or rail grouting.
Grout remains in contact with the underside.
Can be placed in much thinner sections than cementitious grouts, resulting in cost savings.
Good flow characteristics.
UK Conformity Assessed (UKCA).

Consult manufacturer's literature for preparation and mixing guidelines, and CEN flow readings.

Material	Epoxy resin Aggregate
Shape	Formless

Uniclass	Pr_20_31_53_27 Epoxy resin groutsPrimary Pr_20_31_53_52 Metal anchor and fixings grouts
CAWS	E40/430 dowel bars E40/520 Sheet joint filler L30/560 Proprietary balustrades E60/325 Grouting E42/330 Anchor bolts E40/520 Sheet joint filler

Third-party product certification	UK Conformity Assessed (UKCA).

CompressiveStrength	At 10°C: 70 MPa (maximum). At 20°C: 80 MPa (maximum). Guidance for specification option: At 10°C: After 24 hours: 25 MPa, After 3 days: 55 MPa, After 7 days: 70 MPa. At 20°C: After 6 hours: 25 MPa, After 12 hours: 40 MPa, After 24 hours: 60 MPa, After 3 days: 70 MPa, After 7 days: 80 MPa.
Flexural strength	At 10°C: 28 MPa (maximum). At 20°C: 35 MPa (maximum). Guidance for specification option: At 10°C: After 24 hours: 12 MPa, After 3 days: 20 MPa, After 7 days: 28 MPa. At 20°C: After 24 hours: 21 MPa, After 3 days: 29 MPa, After 7 days: 35 MPa.
TensileStrength	At 10°C: 12 MPa (maximum). At 20°C: 17 MPa (maximum). Guidance for specification option: At 10°C: After 24 hours: 5 MPa, After 3 days: 7 MPa, After 7 days: 12 MPa. At 20°C: After 24 hours: 10 MPa, After 3 days: 15 MPa, After 7 days: 17 MPa.
Adhesion bond strength	At 10°C: Dry concrete: 1.95 MPa. Damp concrete: 1.5 MPa. At 20°C: Dry concrete: 2.25 MPa. Damp concrete: 1.85 MPa. Guidance for specification option: After 7 days.
Minimum bearing area	At 10°C: 95%. At 20°C: 90%.
Chemical resistance	Unaffected by a wide range of acids, alkalis and industrial chemicals. Guidance for specification option: Caustic Soda 20%: Unaffected. Hydrochloric Acid 20%: Unaffected. Sulphuric Acid 20%: Unaffected. Detergent: Unaffected. Petrol and Oil: Unaffected.
Application temperature	5–35°C.
Working time	40 minutes up to 5 hours (dependent on temperature).
Standard	To BS EN 1504-3 and -6.