Resin Flooring System FasTop® Multi DP
Verified by manufacturer 6 months ago
Hygienic Polyurethane cement floor screed with aggregate for added slip resistance
Application
For use in:
- Food manufacture and processing.
- Brewing and beverage processing.
- Pharmaceutical manufacturing.
- Heavy duty plant and traffic areas.
- Dairies.
- Commercial kitchens.
- Abattoirs and meat processing.
- Areas requiring high slip resistance.
- Chillers
Description
FasTop Multi DP is a heavy-duty polyurethane cement screed designed to create uniform slip-resistant finishes whilst providing thermal shock resistance for a variety of industrial environments.
FasTop Multi DP is laid between 5-9 mm and then broadcast with quartz, granite or carborundum aggregate to give a heavy non-slip finish designed to provide low slip potential in areas that are wet and/ or exposed to greases and oils. The system is overcoated with FasTop Multi T150 to seal the aggregate in and provide a hard wearing and long-lasting surface. The system is designed to work with the current modular FasTop resins and hardeners.
Features and benefits:
- High or very high slip resistance.
- High chemical resistance.
- Resistant to hot water up to 90 degrees centigrade at 5mm thickness
- Resistant to freezing temperatures
- Hard-wearing.
- Matt finish.
- 22.1 kg pack size.
- 36 month shelf life.
- CE approved.
- FerFa class: 7.
- Light traffic after 12-18 hours
- Full curing time of five to seven days (at 20°C).
- Campden BRI approved as non-taint.
- HACCP certified.
General information
Color | Black Blue Grey Green Red |
Finish | Matt |
Material | Polyurethane Resin Quartz Granite Carborundum |
Shape | Formless |
Length | Bespoke |
Width | Bespoke |
Height | Manufacturer guidance5–7 mm. |
Warranty description | Other |
Uniclass | |
CAWS | M12/110 Resin flooring M12/10 Resin flooring |
Specification data - Resin flooring systems
Substrate | |
Preparation | Preparation of new substrates.Guidance for specification option: New concrete must be clean, sound, dry, fully cured and surface laitance removed by vacuum enclosed shot blasting or mechanical grinding, a minimum strength of 25 N/mm² is required. Preparation of existing substrates.Guidance for specification option: Existing concrete floors: Remove all dirt, oil, grease, old paint or any other surface contaminants by vacuum enclosed shot blasting, scarifying or mechanical grinding. Fats, oils or greases must be removed by mechanical means and detergent washing and making sure all residue of detergent is washed and removed by rinsing with clean water. Local repairs should be carried out using FasTop Multi BU. Existing floors (previously coated): All previous coatings and loose floor paints must be removed by mechanical preparation as described in the above section and primed as specified. If the old resin flooring cannot be removed then please consult with our technical team for advice on intercoat adhesion and suitability, as it may not be compatible with the existing floor coating. |
Levelling screed | FasTop Multi DP. |
Primer | FasTop Multi Primer. |
Resin flooring | Quartz aggregate.Carborundum aggregate.Granite aggregate. |
Overcoating | FasTop Multi T150. |
Shore Hardness - D | To BS ISO 7619-1:2010, 80. |
Abrasion resistance | BS EN 13892-4:2002, AR 4. |
CompressiveStrength | To BS EN 604:2003, 34.6 MPa. |
TensileStrength | BS EN 13892-2:2002, 2.4 N/mm². |
Flexural strength | To BS EN 6319-7:1985, 5.8 N/mm². |
Bond strength | To BS EN 13813, B 3.0. |
Impact resistance | BS EN ISO 6272-1:2011, >4. |
Temperature resistance | Up to 90°C at 5 mm. |
Application temperature | 5–20°C. |
Reaction to fire | To BS EN 13501-1:2018, Bfl–s1. |
System thickness | 5–7 mm. |
Slip resistance | To BS 7976-2:2002+A1:2013, <36 (low slip potential in dry/ wet conditions). |
Coverage | 22.1 kg will cover 2.20 m²/L at 5 mm. |
VOC content | 9 g/L. |
Density | 2 g/cm³ (mixed). |